| ANALYSIS | | TYPICAL | MINIMUM | MAXIMUM |
| Proximate analysis |
| Total moisture | %(as received) |
8.5 | 7 | 1 2 |
|
Ash | % (as received) | 8.71 |
8 | 1 4 |
| Volatiles |
% (as received) | 30.26 | 30 |
36 |
| Sulphur | % (dry basis) |
0. 56 | 0. 4 | 0.9 |
| Net Calorific Value | kcal/kg (as received) |
6 700 | 6500 | 7500 |
| | | | | |
| Size | |
0- 10 0 mm | | |
|
Size distribution |
| + 50.8 mm % 0,1% |
| - 50.8 mm + 25.4 mm % 6.0% MAX - 25.4 mm + 12.7 mm % 8.0%
MAX |
| - 12.7 mm + 0.42 mm % 66.0% MIN - 0,42 mm
% 20.0 % MAX |
| | | | | |
| Free Swelling Index | |
8.5 | | |
| | | | | |
| Ultimate analysis (dry
ash free basis) Reflectance indices RO |
| Carbon
| 85.78 | Average |
0.93 | |
| Oxygen |
5.96 | Minimum | 0.73 | |
| Hydrogen | 5.56 | Maximum
| 1.08 | |
| Nitrogen
| 2.03 | | | |
| | | | | |
| Ash Analysis: |
| Silicon dioxide SiO2 | % |
45.44 | | |
| Aluminium
Oxide Al2O3 | % |
23.80 | | |
| Titanium
TiO2 | % | 0.96 | | |
| Ferric Oxide Fe2O3 | %
| 8.50 | | |
| Calcium Oxide CaO | % |
8.42 | | |
| Sodium
Oxide Na2O | % | 1.41
| | |
| Magnesium
Oxide MnO | % | 2.63 | | |
| Potassium Oxide K2O | % |
1.64 | | |
| Phosphorus
Oxide P2O5 | % |
1.12 | | |
| Sulphur
SO3 | % | 5.64 | | |
| | | | | |
| Temperature: |
| Softening temperature | |
355 oÑ | | |
| Max. Contraction Temperature | |
403 oÑ | | |
| Max. Dilatation Temperature | |
461 oÑ | | |
| Contraction | | -31% | | |
| Dilatation | | +122% | | |
| Initial softening temperature | |
385 oÑ | | |
| Max. Fluidity temperature | |
432 oÑ | | |
| Solidification Temperature | |
469 oÑ | | |
| Maximum Fluidity | | 5910 ddpm
| | |